通过自建的一套空冷凝汽器模拟装置,在模拟其实际运行状况下对可选用的20#钢和3004铝合金管材进行了腐蚀挂片、动态极化曲线和动态电化学阻抗测试等实验,分析了介质温度、溶解氧、pH值和流速对两种材质腐蚀的影响,用SEM、EDS和XRD对腐蚀产物表面膜进行表征分析,由此探讨了其腐蚀机理。结果表明:3004铝合金的腐蚀速率比20#钢小1~2个数量级,且3004铝合金具有非常良好的阻抗特性、生成了均匀致密的耐蚀性氧化膜,而20#钢氧化膜疏松、易脱落、且有腐蚀坑;从技术经济角度上看,3004铝合金具有较好的应用前景。

A device was set up to simulate the actual operation environment of ACC, and then with which, the corrosion behavior of Al-alloy 3004 and carbon steel 20# steel was comparatively studied with the emphasis in the influence of temperature, dissolved oxygen, pH and flow rate of the media on the corrosion of the two materials. After corrosion test, the surface of the two materials was characterized by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), and X- ray diffraction (XRD). The results show that the corrosion rate of 2...